42crmo4 Forgings
1.7725, G41400
42crmo4 Forgings are components manufactured from alloy derived from carbon steel with additions of chromium and molybdenum. 42crmo4 Forgings have a tendency to withstand high temperature service applications. TorqBolt is an eminent 42crmo4 Alloy Steel forged ring supplier in India.
Related Products
42Crmo4 Studs Astm A193 Grade B7 Bolts Astm A193 Grade B7M Bolts Astm A194 Grade 7 Nuts Astm A194 Grade 7M Nuts Astm A320 Grade L7 Bolts Astm A320 Grade L70 Stud Bolts Astm A320 Grade L7M Studs
42crmo4 Forgings Properties
42crmo4 Forgings Chemical Requirements
| Material designation | Chemical composition, % by mass | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Name | Number | C | Si | Mn | P max. |
S max. |
Al tot | B | Cr | Mo | Ni | V | Others |
| 42CrMo4 | 1.7225 | 0,38 to 0,45 | ≤ 0,40 | 0,60 to 0,90 | 0.025 | 0.035 | - | - | 0,90 to 1,20 | 0,15 to 0,30 | - | - | - |
42crmo4 Forgings Mechanical Requirements
Mechanical properties at Room Temperature
Mechanical properties at room temperature for delivery conditions normally applied for further processing
| Material designation | Heat treatment condition a,b | Hardness HBW max. |
Tensile strength Rm MPa max. |
Reduction in area Z % min. |
|
|---|---|---|---|---|---|
| Name | Number | ||||
| 42CrMo4 | 1.7225 | +S | 255 | - | - |
| +A | 241 | - | - | ||
| +AC | - | 630 | 57 | ||
Mechanical properties at room temperature and at 20 °C of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC b
| Material designation | Heat treatment condition a |
Diameter c | Proof strength | Tensile strength | Elongation after fracture | Reduction in area | Impact energy (ISO-V) at 20°C | |
|---|---|---|---|---|---|---|---|---|
| Name | Number | |||||||
| d mm |
Rp0,2 MPa min. |
Rm MPa |
A % min. |
Z % min. |
KV2 J min. |
|||
| 42CrMo4 | 1.7225 | +QT | d ≤ 65 | 730 | 860 to 1 060 | 14 | 50 | 50 |
| 100< di 150 | 420 | 600 to 750 | 18 | 60 | 45 | |||
42crmo4 Proof strength
Minimum 0,2 %-proof strength values at elevated temperature of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC d
| Material designation | Heat treatment condition a | Diameter e d mm |
Minimum 0,2 %-proof strength Rp0,2 in MPa at a temperature (in °C) of: | |||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Name | Number | 50 | 100 | 150 | 200 | 250 | 300 | 350 | 400 | 450 | 500 | 550 | 600 | 650 | ||
| 42CrMo4 | 1.7225 | +QT | d ≤ 60 | 720*) | 702 | 677 | 640 | 602 | 562 | 518 | 475 | 420 | 375 | - | - | - |
| 100 < d ≤ 150 | 414*) | 403*) | 393*) | 382 | 372 | 344 | 324 | 294 | 265 | 226 | - | - | - | |||
42crmo4 Impact Energy
Minimum impact energy (longitudinal direction) at low temperature of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC b
| Material designation | Heat treatment condition a | Diameter e d mm |
Minimum impact energy KV2 in J c (ISO-V test piece) at a test temperature in °C of: |
||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Name | Number | -270 | -196 | -160 | -140 | -120 | -110 | -100 | -90 | -80 | -70 | -60 | -50 | -40 | -20 | 0 | +20 | ||
| 42CrMo4 | 1.7225 | +QT | d ≤ 60 | - | - | - | - | - | - | 27 | - | - | - | - | - | 40 | - | - | 50 |
| 60 < d ≤ 100 | - | - | - | - | - | - | - | - | - | - | - | 40 | 40 | 50 | - | 60 | |||